With patented specialist coatings for galvanised steel, F-AL steel, stainless steel and cast iron, Pohlmetall is synonymous with the highest level of expertise in professional surface finishing. Our innovative coating solutions enable high-performance surfaces without the need for conventional pre-treatments such as phosphating, chromating or pickling.
In this way, Pohlmetall combines technological innovation with efficient processes and high-quality surface finishes, positioning itself as a specialist in forward-looking surface solutions.
ABSORCATION®
| Designation | Absorcation P00969 |
| Application | on steel, stainless steel, and non-ferrous metals, phosphated steels |
| Use | anti-reflective shields, stray light reduction in optical devices, radiation shields, heat protection |
| Coating Thickness | 20 - 50μm |
| Color Tone | black matte |
| Gloss Level | at 60° viewing angle: GU 0–2 |
| Cross-Cut Test | GT0/GT1 |
| Salt Spray Test | 240 hours – depending on the base material |
| Continuous Temperature Resistance | 3300°C – depending on the substrate |
| Outgassing | 0 |
BIOCATION®
| Designation | Biocation P00970 |
| Application | on galvanized and F-AL steels, stainless steel, cast iro |
| Use | exhaust components, heat shields, cooling pipes |
| Coating Thickness | 20 - 50μm |
| Color Tone | black |
| Gloss Level | at 60° viewing angle: GU 3–10 |
| Cross-Cut Test | GT0/GT1 |
| Salt Spray Test | 480 hours – depending on the base material |
| Continuous Temperature Resistance | 300°C – depending on the substrate |
| Outgassing | 0 |
HEATICATION®
| Designation | Heatication P00971 |
| Application | on galvanized and F-AL steels, stainless steel, cast iron |
| Use | not phosphated, chromated, or pickled |
| Coating Thickness | 20–50 μm |
| Color Tone | black matte |
| Gloss Level | at 60° viewing angle: GU 3–8 |
| Cross-Cut Test | GT0/GT0 |
| Salt Spray Test | 720 hours – depending on the base material |
| Continuous Temperature Resistance | up to 650°C – depending on the substrate |
| Outgassing | 0 |
COOLICATION®
| Designation | Coolication P00976 |
| Application | on steel, aluminum, stainless steel |
| Use | heat sinks, heat shields, cooling fins, thermal conductor plates, improvement of cooling efficiency |
| Coating Thickness | 20 - 50μm |
| Color Tone | black satin matte |
| Gloss Level | at 60° viewing angle: GU 3–10 |
| Cross-Cut Test | GT0/GT1 |
| Salt Spray Test | 240 hours – depending on the base material |
| Continuous Temperature Resistance | up to 350°C – depending on the substrate |
| Outgassing | 0 |
PRECICATION 1®
| Designation | Precication 1 P00972 |
| Application | on uncoated steel, aluminum, stainless steel – surface preparation Ra >2.0 |
| Use | precision headlight components – automotive, optical diaphragms, heat shields, heat sinks |
| Coating Thickness | 10–20 μm |
| Color Tone | black matte |
| Gloss Level | at 60° viewing angle: GU 1–5 |
| Cross-Cut Test | GT0/GT1 |
| Salt Spray Test | 480 hours – depending on the base material |
| Continuous Temperature Resistance | 450°C – depending on the substrate |
| Outgassing | 0 |
PRECICATION 2®
| Bezeichnung | Precication 2 P00977 |
| Anwendung | auf verzinkte/ aluminierte Stähle, Edelstahl, Guss |
| Verwendung | Schalldämpfer, Scheinwerferteile, Blenden, Kühlkörper Hitzeschutzbleche, Wärmeleitbleche |
| Schichtdicke | 10 - 20μm |
| Farbton | schwarz-matt |
| Glanzgrad | bei Betrachtungswinkel 60°: GU 1-5 |
| Gitterschnitt | GT0/GT1 |
| Salzsprühtest | 480 Stunden – abhängig vom Grundmaterial |
| Dauertemperatur | bis 450°C – abhängig vom Untergrund |
| Ausgasung | 0 |